Grafting of Cellulose and Microcrystalline Cellulose with Oligo(L-lactic acid) by Polycondensation Reaction

Oligo(L-lactic acid) (OLLA) was synthesized by ring opening polymerization of L-lactides using stannous octoate (0.03 wt% of lactide). While this served as the initiator, L-lactic acids were the co-initiators at 140 °C for 10 h, wherein L-lactic acids were prepared by hydrolytic degradation of L-lactides at 100 °C for 1 h. The molecular weight or degree of polymerization was controlled with monomer/co-initiator ratio (mol/mol). α-cellulose and microcrystalline cellulose (MCC) were extracted from jute fiber by subsequent treatment with sodium chlorite (Na2ClO2), NaOH and H2SO4. Grafting of OLLA onto α-cellulose and MCC in toluene was carried out using para-toluene sulphonic acid as a catalyst and potassium persulphate (KPS) as an initiator at 130 °C under 380 mm (Hg) pressure for 3,…