Synthesis and characterization of ZnFe2O4 nanoparticles and its biomedical applications

Biomedical applications of ZnFe2O4 nanoparticle are preferable among all kinds of ferrites due to the compatibility of Zn2+ ions for human bodies. We have followed the soft chemical route to synthesize chitosan and PEG coated ZnFe2O4 nanoparticles and also the chitosan-coated-nanoparticles encapsulated with liposome. X-ray diffraction studies by the Mo Kα target, showed the formation of single phase spinel structure. The lattice parameter turned out to be 8.48Å and grain size ~ 4.8 nm (± 0.1 nm). Similar particle size was observed by transmission electron microscope analysis. HRTEM studies showed the distinct lattice fringes thus confirming the good crystallinity of the synthesized nanoparticles. M-H curve at room temperature showed the prepared sample was superparamagnetic in nature, which is also confirmed…